鋁板加工過程中常常會(huì)因?yàn)檎蹚澏斐射X板斷裂，尤其是折彎好后做陽極氧化處理的崩裂，更讓許多鋁板生產(chǎn)加工公司疑惑，那麼如何應(yīng)對(duì)那樣的問題產(chǎn)生呢，我們一起來剖析下鋁板加工如何避免折彎開裂。
In the process of aluminum plate processing, aluminum plate fracture is often caused by bending, especially the cracking of anodizing treatment after bending, which makes many aluminum plate production and processing companies wonder, so how to deal with such problems? Let's analyze how to avoid bending cracking in aluminum plate processing.
造成鋁板加工如何避免折彎開裂斷裂緣故實(shí)際上關(guān)鍵下列這幾個(gè)方面，如果我們?cè)诩庸み^程中留意下列問題，就會(huì)大大減少斷裂的產(chǎn)生。

How to avoid bending cracking and fracture in aluminum plate processing actually depends on the following aspects. If we pay attention to the following problems in the processing process, the occurrence of fracture will be greatly reduced.
一. 鋁板的強(qiáng)度太高。通常狀況越硬的物件，越非常容易受外力作用危害斷裂，鋁板也是一樣，因此我們?cè)谔暨x鋁板時(shí)一定要選好鋁板，依據(jù)鋁板型號(hào)和情況來挑選這些更非常容易折彎的商品，像鋁板中1系列產(chǎn)品、3系列、5系列產(chǎn)品型號(hào)商品就很容易折彎，而6系列產(chǎn)品、7產(chǎn)品系列因?yàn)閺?qiáng)度太高，必須做退火處理到O態(tài)后才好折彎。
I The strength of aluminum plate is too high. Generally, the harder the object is, the more likely it is to be damaged and broken by external force, and so is the aluminum plate. Therefore, when selecting the aluminum plate, we must select the aluminum plate, and select these products that are more easy to bend according to the aluminum plate model and situation. For example, the products of series 1, series 3 and series 5 in the aluminum plate are easy to bend, while the products of series 6 7 because the strength of the product series is too high, it must be annealed to o state before bending.
二.鋁板的薄厚。鋁板越厚越不容易折彎，和其它原材料一樣，因此我們?cè)谔暨x時(shí)，可以考量挑選薄鋁板來生產(chǎn)加工商品，防止斷裂產(chǎn)生。
II Thickness of aluminum plate. The thicker the aluminum plate, the less easy it is to bend. Like other raw materials, we can consider selecting thin aluminum plates to produce and process goods to prevent fracture.
三.折彎視角和鋁板花紋。無論啥子物件折彎視角越大，通過率會(huì)越高，因此我們?cè)阡X板生產(chǎn)加工時(shí)，折彎視角盡量的大，再有就是鋁板花紋，折彎方位要與鋁板花紋方位豎直，不可以平行面。
III Bending angle and aluminum plate pattern. The larger the bending angle of any object, the higher the passing rate. Therefore, when we produce and process aluminum plate, the bending angle should be as large as possible. In addition, the aluminum plate pattern. The bending direction should be vertical with the aluminum plate pattern, and cannot be parallel.
在鋁板加工如何避免折彎開裂過程中如果我們可以防止以上幾個(gè)人難點(diǎn)，鋁板折彎斷裂的就會(huì)極大地降低，鋁板生產(chǎn)廠家問題會(huì)獲得不錯(cuò)的處理。
In the process of how to avoid bending cracking in aluminum plate processing, if we can prevent the above difficulties, the of aluminum plate bending fracture will be greatly reduced, and the problems of aluminum plate manufacturers will be well handled.